ASTM A335 P22 Pipe is the part of ASTM A335, The pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding. The steel material shall conform to chemical composition, tensile property, and hardness requirements.
ASTM A335 P22 Pipe is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Sometimes referred to as "P Grade”, chome moly pipe is popular in P-Grades P5, P9, P11, P22, and P91. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries
A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (Mo) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability. Moly increases the resistance to softening, restrains grain growth and makes chromium steel less susceptible to embrittlement. Moly is the most effective single additive that increases high temperature creep strength. It also enhances the corrosion resistance of steel, and inhibits pitting. Chromium (or chrome) is the essential constituent of stainless steel. Any steel with 12% or more Chrome is considered stainless.
Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and hardness at room temperatures. The composition chrome moly alloy steel pipe make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.
Prosaic Steel Supply stocks a full range of the following ASTM A335 pipe grades:
Size Range | 1/8″ –42” |
Schedules | 20, 30, 40, Standard (STD), Extra Heavy (XH), 80, 100, 120, 140, 160, XXH & heavier |
Standard | ASTM A335, ASME SA335, ASTM A213, ASTM A691, ASME SA691 |
Grade | ASTM A335 P1, ASTM A335 P2, ASTM A335 P5, ASTM A335 P9, ASTM A335 P11, ASTM A335 P12,ASTM A335 P22, ASTM A335 P23, ASTM A335 P91, ASTM A335 P92, ASTM A213 T2,ASTM A213 T5, ASTM A213 T5b,ASTM A213 T5c, ASTM A213 T9, ASTM A213 T11, ASTM A213 T12, ASTM A213 T22, ASTM A213 T23, ASTM A213 T91, ASTM A213 T92 |
ASTM A335 P5 Pipe | ASTM A335 P9 Pipe | ASTM A335 P11 Pipe |
ASTM A335 P12 Pipe | ASTM A335 P22 Pipe | ASTM A335 P91 Pipe |
ASTM A335 P22 Pipe offered by us are made as per IBR standards and are used mainly for boiler operations. We source these seamless pipes in varied size range. Further, we can also get these customized as per boiler piping requirements. For ensuring in them optimum quality standards, we source these from quality manufacturers. We also offer clients of having their own mark on them.
Chemical composition % of A335 P22 Alloy Steel Seamless Pipe
Compositions | Data |
UNS Designa-tion | K21590 |
Carbon | 0.05-0.15 |
Manganese | 0.30-0.60 |
Phosphorus(max.) | 0.025 |
Sulfur(max.) | 0.025 |
Silicon | 0.50-1.00 |
Nickel | … |
Chromium | 1.90-2.60 |
Molybdenum | 0.87-1.13 |
Other Elements | … |
Tensile Strength, MPa | Yield Strength, MPa | Elongation, % |
415 min | 205 min | 30 min |
P5, P9, P11 and P22 | |||
Grade | Heat Treatment Type | Normalizing Temperature Range F [C] | Subcritical Annealing or Tempering Temperature Range F [C] |
P5 (b,c) | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
Subcritical Anneal (P5c only) | ***** | 1325 - 1375 [715 - 745] | |
P9 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
P11 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1200 [650] | |
P22 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
P91 | Normalize and Temper | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Quench and Temper | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Tensile Strength, MPa | Yield Strength, MPa | Elongation, % |
415 min | 205 min | 30 min |
P5, P9, P11 and P22 | |||
Grade | Heat Treatment Type | Normalizing Temperature Range F [C] | Subcritical Annealing or Tempering Temperature Range F [C] |
P5 (b,c) | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
Subcritical Anneal (P5c only) | ***** | 1325 - 1375 [715 - 745] | |
P9 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
P11 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1200 [650] | |
P22 | Full or isothermal Anneal | ||
Normalize and Temper | ***** | 1250 [675] | |
P91 | Normalize and Temper | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
Quench and Temper | 1900-1975 [1040 - 1080] | 1350-1470 [730 - 800] |
NPS [DN] Designator | Tolerance, % from Specified | |
Over | Under | |
1/8 to 2 1/2 [6 to 65] incl., all t/D ratios | 20.0% | 12.5% |
Above 2 1/2 [65], t/D < or = 5% | 22.5% | 12.5% |
Above 2 1/2 [65], t/D > 5% | 15.0% | 12.5% |
(t = Specified Wall Thickness; D = Specified Outside Diameter) |
Calculated Minimum Elongation Values | |||||
Elongation in 2 in. or 50 mm, min % | |||||
Wall Thickness | P5, P9, P11, P22 | P91 | |||
in. | mm | Longitudinal | Transverse | Longitudinal | |
5/16 (0.312) | 8 | 30 | 20 | 20 | |
9/32 (0.281) | 7.2 | 28 | 19 | 19 | |
1/4 (0.250) | 6.4 | 27 | 18 | 18 | |
7/32 (0.219) | 5.6 | 26 | 17 | ||
3/16 (0.188) | 4.8 | 24 | 16 | ||
5/32 (0.156) | 4 | 22 | 15 | ||
7/8 (0.125) | 3.2 | 21 | 14 | ||
3/32 (0.094) | 2.4 | 20 | 13 | ||
1/18 (0.062) | 1.6 | 18 | 12 |
Outside Diameter at any point shall not vary from standard specified more than:
NPS [DN] Designator | Over | Under | ||
in. | mm | in. | mm | |
1/8 to 1 1/2 [6 to 40], incl. | 1/64 (0.015) | 0.40 | 1/64 (0.015) | 0.40 |
Over 1 1/2 to 4 [40 to 100], incl. | 1/32 (0.031) | 0.79 | 1/32 (0.031) | 0.79 |
Over 4 to 8 [100 to 200], incl. | 1/16 (0.062) | 1.59 | 1/32 (0.031) | 0.79 |
Over 8 to 12 [200 to 300], incl. | 3/32 (0.093) | 2.38 | 1/32 (0.031) | 0.79 |
Over 12 [300] | +/- 1% of the specified outside diameter |
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test | |
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested. | |
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe. | |
Notes for Hardness Test: | P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC]. |
Notes for Bend Test: | For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test. |
Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser. | |
The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion. | |
The inside diameter of the bend shall be 1 inch [25 mm]. | |
Hydrostatic Test | Each length of pipe shall be Hydro tested, at option of manufacture nondestructive electric testing can be used. |
(On Tags attached to each Bundle in case of Bundled Pipe) Markings will adhere to prescribed specifications in A 999/A999M and be: Rolled, Stamped, or Stenciled (Mfrs. Option)
In addition, markings will include: | ||||||||||||||||||||||||||
Length of Pipe |
|
|||||||||||||||||||||||||
Schedule Number | ||||||||||||||||||||||||||
Heat Number or Manufacturer’s number by which heat can be identified | ||||||||||||||||||||||||||
An Additional Symbol "S” if the pipe conforms to any Supplementary Requirements | ||||||||||||||||||||||||||
S1 – Product Analysis | ||||||||||||||||||||||||||
S2 – Transverse Tension Test | ||||||||||||||||||||||||||
S3 – Flattening Test | ||||||||||||||||||||||||||
S4 – Metal Structure and Etching Tests | ||||||||||||||||||||||||||
S5 – Photomicrographs | ||||||||||||||||||||||||||
S6 – Photomicrographs for Individual Pieces | ||||||||||||||||||||||||||
S7 – Alternative Heat Treatment – Grade P91 | ||||||||||||||||||||||||||
Pipe that has been weld repaired shall be marked "WR”. |
Orders for material under this specification should include the following, as required, to describe the desired material adequately:
Quantity | Feet, meters, or number of lengths |
Name of material | Seamless Alloy Steel Pipe |
Grade | P5, P9, P11, P22, P91 |
Manufacturer | Hot-finished or cold-drawn |
Size using one of the following: | |
NPS and Schedule Number | |
Outside Diameter and Nominal Wall Thickness | |
Outside Diameter and Minimum Wall Thickness | |
Inside Diameter and Nominal Wall Thickness | |
Inside Diameter and Minimum Wall Thickness | |
Length | Specific or Random |
End Finish |
A335 Grade P22 Pipe is sleeved into plastic bag individually, pieces wrapped with water-proof material, bundled with nylon rope. Clear labels are tagged on the outside of the package for easy identification of the quantity and product I.D. Great care is taken during operation and transportation.
A335 Grade P22 Pipe packing will be according to international standard in bundles strapped by strips then into containers to avoid any damage.
Delivery: Within 10-25 days or asap if we have enough stock
We export ASTM A335 P22 Pipe to Saudi Arabia, Iran, Iraq, United Arab Emirates, Qatar, Bahrain, Oman, Kuwait, Turkey, Egypt, Yemen, Syria, israel, Jordan, Cyprus, Singapore, Malaysia, Indonesia, Thailand, Vietnam, South Korea, Japan, Sri Lanka, Maldives, Bangladesh, Mayanmar, Taiwan, Cambodia, Argentina, Bolivia, Brazil, Chile, Venezuela, Colombia, Ecuador, Guyana, Paraguay, Uruguay, United States Of America, Canada, Mexico, Panama, Costa Rica, Puerto Rica, Trinidad And Tobago, Jamaica, Bahamas, Denmark, Russia, Norway, Germany, France, Italy, United Kingdom, Spain, Ukraine, Netherland, Belgium, Greece, Czech Republic, Portugal, Hungary, Albania, Austria, Switzerland, Slovakia, Finland, Ireland, Croatia, Slovenia, Malta, Nigeria, Algeria, Angola, South Africa, Libya, Egypt, Sudan, Equatorial Guinea, The Republic of Congo, Gabon, Europe, Africa, Asia, North America, South America, Middle East, Far East etc.
Prosaic Steel and Alloys is a well known worldwide exporter of ASTM A335 P22 Pipe, Prosaic Steel and Alloys is committed to provide each and every customer with the highest standard of customer service. We deals in ASTM A335 P22 Pipe in India & Overseas, offering a wide range of ASTM A335 Grade P22 Alloy Steel Seamless Pipe and Tube
Prosaic Steel and Alloys is Leading Manufacturer, Distributor, Exporter, Stockholder and Supplier of ASTM A335 P22 Pipe in United States of America (USA), Saudi Arabia, Italy, Netherlands, Germany, Canada, Singapore, Malaysia, Indonesia