ASTM A335 Pipes specification covers nominal wall and minimum wall seamless ferritic alloy-steel pipe intended for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding
ASTM A335 Pipe (ASME S/A335, Chorme-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Sometimes referred to as "P Grade”, chome moly pipe is popular in P-Grades P5, P9, P11, P22, and P91. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries
A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (Mo) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability. Moly increases the resistance to softening, restrains grain growth and makes chromium steel less susceptible to embrittlement. Moly is the most effective single additive that increases high temperature creep strength. It also enhances the corrosion resistance of steel, and inhibits pitting. Chromium (or chrome) is the essential constituent of stainless steel. Any steel with 12% or more Chrome is considered stainless.
Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and hardness at room temperatures. The composition chrome moly alloy steel pipe make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.
Grades: P-5, P-9, P-11, P-12, P-22, and P-91
NPS 1/4'' to NPS 48''
Wall Thickness - Schedules 40 through 160, STD, XS, XXS.
Unscheduled heavy wall pipe thicknesses available up to 4 inches.
|ASTM A335 P5 Pipe||ASTM A335 P9 Pipe||ASTM A335 P11 Pipe|
|ASTM A335 P12 Pipe||ASTM A335 P22 Pipe||ASTM A335 P91 Pipe|
Alloy Steel Seamless Pipes (IBR) offered by us is made of alloy steel and feature exceptional performance properties. These are developed for energy-related applications involving oil & gas drilling and therefore are subjected to stresses in machine parts. Further, Alloy Steel Tubes are also used in domestic, professional or industrial areas.
Alloy Steel Seamless Pipes (ASME SA335 Grade P5)
Alloy Steel Seamless Pipes (ASME SA335 Grade P5) offered by us are made available in ASME SA335 as well as P1, P5, P9, P11, P12, P91 grades. Our expertise lies in offering these in different sizes & schedules, with IBR & latest edition NACE MR 0175 reports.
ASME Alloy Steel Seamless Tubes/ Pipes (SA335 Grade P9)
ASME Alloy Steel Seamless Tubes/ Pipes (SA335 Grade P9) manufactured, supplied and exported by us are used for various industrial applications. Our specialization in offering precision engineered alloy steels allow us to deliver these for various engineering applications in various grades like A-387 GR. P1, P5, P9, P11, P12, P22, P91, ASTM A-335 and others. The other specifications include:
Alloy Steel Pipes (ASTM A335 P11)
Alloy Steel Pipes (ASTM A335 P11) offered by us are made as per IBR standards and are used mainly for boiler operations. We source these seamless pipes in varied size range. Further, we can also get these customized as per boiler piping requirements. For ensuring in them optimum quality standards, we source these from quality manufacturers. We also offer clients of having their own mark on them.
Alloy Steel Pipes (ASTM A335 P12)
Alloy Steel Pipes (ASTM A335 P12) offered by us are available with ASTM A335 P12 standard and finds application in industries like Petrochemicals, Refineries, Fertilizers, Pharmaceuticals and others. We can source these seamless pipes in size range of up to 26 inches.
Alloy Seamless Pipes (ASTM A335 Grade P91 NACE)
ASTM A335 Grade P91 Pipe NACE offered by us are made available in ASTM A335 Grades. Made as per IBR standards, these are mainly used in boiler operations. Further, our expertise lies in offering these pipes in various size range as well as in customized parameters as per boiler piping requirements. Sourced from quality conscious manufacturers, we also offer our clients the option of adding their own mark on them.
|P5, P9, P11 and P22|
|Grade||Heat Treatment Type||Normalizing Temperature Range F [C]||Subcritical Annealing
Temperature Range F
|P5 (b,c)||Full or isothermal Anneal|
|Normalize and Temper||*****||1250 |
|Subcritical Anneal (P5c only)||*****||1325 - 1375 [715 - 745]|
|P9||Full or isothermal Anneal|
|Normalize and Temper||*****||1250 |
|P11||Full or isothermal Anneal|
|Normalize and Temper||*****||1200 |
|P22||Full or isothermal Anneal|
|Normalize and Temper||*****||1250 |
|P91||Normalize and Temper||1900-1975 [1040 - 1080]||1350-1470 [730 - 800]|
|Quench and Temper||1900-1975 [1040 - 1080]||1350-1470 [730 - 800]|
|Grade||P-5||P-9||P-11||P-22||P-91||P-91 shall also include the following:|
|Carbon||0.15 max||0.15 max||0.05 - 0.15||0.05 - 0.15||0.08 - 0.12||V at 0.18 - 0.25|
|Manganese||0.30 - 0.60||0.30 - 0.60||0.30 - 0.60||0.30 - 0.60||0.30 - 0.60||N at 0.030 - 0.070|
|Phosphorous, max||0.025||0.025||0.025||0.025||0.020||Ni at 0.40 max|
|Sulfur, max||0.025||0.025||0.025||0.025||0.010||Al at 0.02 max|
|Silicon||0.50 max||0.25 - 1.00||0.50 - 1.00||0.50 max||0.20 -0.50||Cb at 0.06 - 0.10|
|Chromium||4.00 - 6.00||8.00 - 10.00||1.00 - 1.50||1.90 - 2.60||8.00 - 9.50||Ti at 0.01 max|
|Molybdenum||0.45 -0.65||0.90 - 1.10||0.44 - 0.65||0.87 - 1.13||0.85 - 1.05||Zr at 0.01 max|
|P-5||P-9||P-11||P-22||P-91||P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].|
|Tensile Strength, min., psi|
|Yield Strength, min., psi|
|NPS [DN] Designator||Tolerance, % from Specified|
|1/8 to 2 1/2 [6 to 65] incl., all t/D ratios||20.0%||12.5%|
|Above 2 1/2 , t/D < or = 5%||22.5%||12.5%|
|Above 2 1/2 , t/D > 5%||15.0%||12.5%|
|(t = Specified Wall Thickness; D = Specified Outside Diameter)|
|Calculated Minimum Elongation Values|
|Elongation in 2 in. or 50 mm, min %|
|Wall Thickness||P5, P9, P11, P22||P91|
Outside Diameter at any point shall not vary from standard specified more than:
|NPS [DN] Designator||Over||Under|
|1/8 to 1 1/2 [6 to 40], incl.||1/64 (0.015)||0.40||1/64 (0.015)||0.40|
|Over 1 1/2 to 4 [40 to 100], incl.||1/32 (0.031)||0.79||1/32 (0.031)||0.79|
|Over 4 to 8 [100 to 200], incl.||1/16 (0.062)||1.59||1/32 (0.031)||0.79|
|Over 8 to 12 [200 to 300], incl.||3/32 (0.093)||2.38||1/32 (0.031)||0.79|
|Over 12 ||+/- 1% of the specified outside diameter|
|Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test|
|For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.|
|For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.|
|Notes for Hardness Test:||P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].|
|Notes for Bend Test:||For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.|
|Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.|
|The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.|
|The inside diameter of the bend shall be 1 inch [25 mm].|
|Hydrostatic Test||Each length of pipe shall be Hydro tested, at option of manufacture nondestructive electric testing can be used.|
Note: (S)A335 P91 other chemical composition are : V 0.18~0.25; N 0.030~0.070; Ni ≤ 0.40; Al ≤ 0.04 ; Nb 0.06~0.10
(S)A335 P92 other chemical composition are : V 0.15~0.25; N 0.030~0.070; Ni ≤ 0.40; Al ≤ 0.04 ; Nb 0.04~0.09; W 1.5~2.00 ; B 0.001~0.006
A335 Grade P5, P9, P11, P22, P91 Alloy Steel Seamless Pipe and Tube Packing
A335 Grade P5, P9, P11, P12, P22, P91 Alloy Steel Seamless Pipe and Tube is sleeved into plastic bag individually, pieces wrapped with water-proof material, bundled with nylon rope. Clear labels are tagged on the outside of the package for easy identification of the quantity and product I.D. Great care is taken during operation and transportation.
A335 Grade P5, P9, P11, P12, P22, P91 Alloy Steel Seamless Pipe packing will be according to international standard in bundles strapped by strips then into containers to avoid any damage.
Delivery: Within 10-25 days or asap if we have enough stock
We export ASTM A335 Pipe to Saudi Arabia, Iran, Iraq, United Arab Emirates, Qatar, Bahrain, Oman, Kuwait, Turkey, Egypt, Yemen, Syria, israel, Jordan, Cyprus, Singapore, Malaysia, Indonesia, Thailand, Vietnam, South Korea, Japan, Sri Lanka, Maldives, Bangladesh, Mayanmar, Taiwan, Cambodia, Argentina, Bolivia, Brazil, Chile, Venezuela, Colombia, Ecuador, Guyana, Paraguay, Uruguay, United States Of America, Canada, Mexico, Panama, Costa Rica, Puerto Rica, Trinidad And Tobago, Jamaica, Bahamas, Denmark, Russia, Norway, Germany, France, Italy, United Kingdom, Spain, Ukraine, Netherland, Belgium, Greece, Czech Republic, Portugal, Hungary, Albania, Austria, Switzerland, Slovakia, Finland, Ireland, Croatia, Slovenia, Malta, Nigeria, Algeria, Angola, South Africa, Libya, Egypt, Sudan, Equatorial Guinea, The Republic Of Congo, Gabon, Europe, Africa, Asia, North America, South America, Middle East, Far East etc.
Prosaic Steel and Alloys is a well known worldwide exporter of ASTM A335 Pipe, Prosaic Steel and Alloys is committed to provide each and every customer with the highest standard of customer service. We deals in ASTM A335 Pipe and Tubes in India & Overseas, offering a wide range of ASTM A335 Alloy Steel Seamless Pipe
Prosaic Steel and Alloys is Leading Manufacturer, Distributor, Exporter, Stockholder and Supplier of ASTM A335 Pipe in United States of America (USA), Saudi Arabia, Italy, Netherlands, Germany, Canada, Singapore, Malaysia, Indonesia